Cold work tool steel
ALTA 1.2510 Tool Steel Specification
Steel properties
ALTA 1.2510 steel is an oil hardening tool steel supplied in the annealed condition. It offers good durability, gives excellent abrasive wear resistance which compared than 1.2842 tool steel. With these properties this ALTA 1.2510 tool steel is an excellent general purpose grade often used where the expense of a high carbon high chromium tool steel would not be justified
Applications
² Wear-resistant non-deformable cold mold (such as sheet stamping dies, embossing dies for jewelry)
² All kinds of metal stamping die and forming tools (such as notches cutting die, die sleeve)
² Cutting tools, wood or paper industry working cutting tools/machine knives
² Making of aluminum, zinc and copper alloy extrusion dies, casting dies and hot shearing blades
² Small silver Polish steel (scaled and cold drawn), which is an ideal material for ejection pins and sleeves
Chemical composition
Chemical Composition per %
|
C |
Si |
Mn |
P |
S |
Cr |
W |
V |
Ni |
Cu |
Min. |
0.90 |
0.15 |
1.00 |
|
|
0.50 |
0.50 |
0.10 |
|
|
Max. |
1.05 |
0.35 |
1.20 |
0.030 |
0.030 |
0.70 |
0.70 |
0.15 |
0.25 |
0.30 |
Basic melting process : |
IM/EAF + LF + VD + (ESR) |
Hardness : |
Max 230 HB (annealed) |
Reduction ratio : |
5 : 1 minimum or required |
Grain size : |
≥ 6.0 per ASTM E112 |
Non-metallic inclusion : |
≤ 1.0 (thick), ≤ 1.5 (thin) per ASTM E45 method A (more pure by ESR route) |
Ultrasonic Test |
SEP1921, , EN 10308, ASTM A388 or agreed methods |
Macro-structure |
As per ASTM E381 |
Straightness / flatness |
≤ 1.5 mm / m (machined), ≤ 2.5 mm / m (black) |
Tolerance |
Per discussed |
Size range (round bars) |
Ø 12 - 500 mm |
Size range (flats, plates) |
8 - 400 mm in thickness max. 1100 mm in width |
Downloads
-
2024-06-25 Alta 1.2510 SPEC (011 - S6 - T2 ).pdf
끂33 249.51 KB
² Very high compressive strength
² High toughness and ductility
² High grindability
² Good wear resistance
² Good dimensional stability
Features